Abstract: There is increasing interest in the degradation studies of thermal and environmental barrier coatings (TEBCs) of gas turbines by molten CaO-MgO-Al2O3-SiO2 (CMAS). CMAS minerals are usually referred as silica-containing sand dust and volcano ash materials that are carried by the intake air into gas turbines, e.g. aircraft engines. The low-melting deposits react at high temperatures (1000C) with the coating materials. This causes degradation and accelerated coating failure of the static and rot…