Abstract: A protective ductile NiCr coating has shown promise to mitigate oxidation and corrosion attack on superalloy disk alloys. The effects of this coating on fatigue life and failure modes of the disk superalloy are an important concern. The objective of this study was to investigate the fatigue life and failure modes of disk superalloy specimens protected by this coating, using varied pre-coating and post-coating processes. Cylindrical gage fatigue specimens of a powder metallurgy-processed disk …